Methods of forming materials over uneven surface topologies, and methods of forming insulative materials over and between conductive lines

ABSTRACT

In one aspect, the invention encompasses a semiconductor processing method of forming a material over an uneven surface topology. A substrate having an uneven surface topology is provided. The uneven surface topology comprises a valley between a pair of outwardly projecting features. A layer of material is formed over the uneven surface topology. The layer comprises outwardly projecting portions over the outwardly projecting features of the surface topology and has a gap over the valley. The layer is etched, and the etching forms protective material within the gap while removing an outermost surface of the layer. The etching substantially does not remove the material from the bottom of the gap. In another aspect, the invention encompasses a semiconductor processing method of forming a material over metal-comprising lines. A first insulative material substrate is provided. A pair of spaced metal-comprising lines are formed over the substrate. The spaced metal-comprising lines define an uneven surface topology which comprises the lines and a valley between the lines. A layer of second insulative material is formed over the uneven surface topology. The layer comprises outwardly projecting portions over the lines and having a gap over the valley. The layer of second insulative material is subjected to an etch which forms a protective material at the bottom of the gap. The protective material substantially prevents the second insulative material from being etched from the bottom of the gap.

TECHNICAL FIELD

[0001] The invention pertains to methods of reducing non-planarity of surfaces, and, in particular applications, pertains to methods of forming materials over uneven surface topologies. In exemplary embodiments, the invention pertains to methods of forming insulative materials over and between conductive lines.

BACKGROUND OF THE INVENTION

[0002] A prior art method of forming insulative material over and between conductive lines is described with reference to FIGS. 1-4. Referring to FIG. 1, a fragment 10 is illustrated at a preliminary processing step. Fragment 10 comprises a substrate 12 having an upper surface 15. Conductive lines 14, 16, 18 and 20 are formed over upper surface 15. Substrate 12 can comprise an insulative material such as, for example, borophosphosilicate glass (BPSG), silicon dioxide and/or silicon nitride. Substrate 12 can further include a portion of a semiconductive material wafer. To aid in interpretation of the claims that follow, the term “semiconductive substrate” is defined to mean any construction comprising semiconductive material, including, but not limited to, bulk semiconductive materials such as a semiconductive wafer (either alone or in assemblies comprising other materials thereon), and semiconductive material layers (either alone or in assemblies comprising other materials). The term “substrate” refers to any supporting structure, including, but not limited to, the semiconductive substrates described above.

[0003] Conductive lines 14, 16, 18 and 20 can comprise conductively doped polysilicon and/or metals. Exemplary metals are aluminum, aluminum alloys, copper, copper alloys, tungsten and titanium. In particular aspects, conductive lines 14, 16, 18 and 20 can consist essentially of metals (either in alloy form or elemental form). Such metallic conductive lines can further correspond to a first elevational level of metallic conductive lines formed over a semiconductive substrate (a so-called “metal 1” layer).

[0004] An insulative material 22 is formed over and between conductive lines 14, 16, 18 and 20. Material 22 can comprise, for example, silicon dioxide, and can be formed by chemical vapor deposition (CVD) utilizing a tetraorthosilicate (TEOS) precursor. Such CVD can occur at or below 400° C., which can be advantageous to avoid melting of any metals incorporated into lines 14, 16, 18 and 20.

[0005] In the construction of FIG. 1, material 22 is formed over an uneven surface topology. Such uneven surface topology comprises outward projecting features consisting of lines 14, 16, 18 and 20, and valleys 24 consisting of spaces between lines 14, 16, 18 and 20. The deposited material 22 comprises outwardly projecting features 26 over conductive lines 14, 16, 18 and 20, and comprises gaps 28 over valleys 24. The gaps 28 have bottoms 23 extending elevationally beneath uppermost surfaces of conductive lines 14, 16, 18, and 20. Material 22 thus comprises a substantially non-planar outer surface 30 which extends over lines 14, 16, 18 and 20, and within gaps 28. Outer surface 30 comprises substantially horizontal upper surfaces 27 and substantially vertical sidewall surfaces 29.

[0006] It is noted that a continuing goal of semiconductor fabrication is to decrease the size of circuit elements. Lines 14, 16, 18 and 20 have respective widths “Y” (shown for lines 16 and 18), and gaps 24 have about the same respective widths “Y”. The width “Y” will typically correspond to about a minimum feature width achievable during fabrication of lines 14, 16, 18 and 20.

[0007] Present semiconductor fabrication processes achieve constructions in which “Y” is about 0.5 micron and, of course, a goal of future processes is to achieve constructions in which “Y” is less than 0.5 micron. The 0.5 micron spacing corresponding to gaps 24 is too tight to allow material 22 to form conformally over and between lines 14, 16, 18 and 20. If material 22 formed conformally over and between lines 14, 16, 18 and 20, gaps 28 would be relatively wide shallow gaps. Instead, gaps 28 have a high aspect ratio (i.e., an aspect ratio of at least about 3), which complicates further processing. Specifically, it is frequently desired to planarize material 22 to form material 22 into a substantially level base which can be utilized to support additional circuitry formed above it. A common method of planarization is chemical-mechanical polishing. However, such will not work effectively on the material 22 shown in FIG. 1 because the chemical-mechanical processing will be stopped before removing the material of lines 14, 16, 18 and 20, and hence before reaching the bottoms 23 of gaps 28. Accordingly, portions of gaps 28 will remain after a chemical-mechanical polishing process, and will cause a remaining portion of material 22 to have a non-planar outer surface.

[0008] In an effort to overcome the above-described difficulties in planarizing material 22, the processing of FIGS. 2-4 is employed. FIG. 2 illustrates fragment 10 after material 22 has been subjected to an anisotropic etch. Such etch forms material 22 into sidewall spacers 40 extending along sidewalls of conductive lines 14, 16, 18 and 20. The etching also widens gaps 28. Additionally, the etching can, as shown, extend gaps 28 into underlying material 12. The extent to which gaps 28 penetrate into material 12 depends on how selective the anisotropic etch is for material 22 relative to the material of substrate 12. If material 22 and substrate 12 comprise the same material (such as, for example, BPSG), then the etch will be non-selective for material 22 relative to the underlying material substrate 12.

[0009] Referring to FIG. 3, additional layers 42 and 44 are formed over conductive lines 14, 16, 18 and 20, and within gaps 28. Materials 42 and 44 comprise insulative materials such as, for example, silicon dioxide or BPSG. Materials 22 and 24 fill gaps 28 to a level above lines 14, 16, 18 and 20.

[0010] Referring to FIG. 4, materials 42 and 44 can be subjected to chemical-mechanical polishing to form a planarized insulative material having an upper surface above lines 14, 16, 18 and 20.

[0011] It would be desirable to develop alternative methods for forming a planarized material. More generally, it would be desirable to develop new methods of forming and planarizing materials formed over uneven surface topologies.

SUMMARY OF THE INVENTION

[0012] In one aspect, the invention encompasses a semiconductor processing method of forming a material over an uneven surface topology. A substrate having an uneven surface topology is provided. The uneven surface topology comprises a valley between a pair of outwardly projecting features. A layer of material is formed over the uneven surface topology. The layer comprises outwardly projecting portions over the outwardly projecting features of the surface topology and has a gap over the valley. The layer is etched. The etching forms protective material within the gap while removing an outermost surface of the layer. The etching substantially does not remove the material from the bottom of the gap.

[0013] In another aspect, the invention encompasses a semiconductor processing method of forming a material over metal-comprising lines. A first insulative material substrate is provided. A pair of spaced metal-comprising lines are formed over the substrate. The spaced metal-comprising lines define an uneven surface topology which comprises the lines and a valley between the lines. A layer of second insulative material is formed over the uneven surface topology. The layer comprises outwardly projecting portions over the lines and having a gap over the valley. The layer of second insulative material is subjected to an etch which forms a protective material at the bottom of the gap. The protective material substantially prevents the second insulative material from being etched from the bottom of the gap.

BRIEF DESCRIPTION OF THE DRAWINGS

[0014] Preferred embodiments of the invention are described below with reference to the following accompanying drawings.

[0015]FIG. 1 is a diagrammatic, fragmentary, cross-sectional view of a substrate at a preliminary step of a prior art processing method.

[0016]FIG. 2 is a view of the FIG. 1 substrate at a prior art processing step subsequent to that of FIG. 1.

[0017]FIG. 3 is a view of the FIG. 1 substrate at a prior art processing step subsequent to that of FIG. 2.

[0018]FIG. 4 is a view of the FIG. 1 substrate at a prior art processing step subsequent to that of FIG. 3.

[0019]FIG. 5 is a diagrammatic, fragmentary, cross-sectional view of a substrate at a preliminary step of a first embodiment method of the present invention, with such step occurring after the prior art processing of FIG. 1.

[0020]FIG. 6 is a view of the FIG. 5 substrate at a processing step subsequent to that of FIG. 5.

[0021]FIG. 7 is a view of the FIG. 5 substrate at a processing step subsequent to that of FIG. 6.

[0022]FIG. 8 is a view of the FIG. 5 substrate at a processing step subsequent to that of FIG. 7.

[0023]FIG. 9 is a diagrammatic, fragmentary, cross-sectional view of a substrate at a preliminary step of a second embodiment method of the present invention, with such step occurring after the prior art processing of FIG. 1.

[0024]FIG. 10 is a diagrammatic, fragmentary, cross-sectional view of a substrate at a preliminary step of a third embodiment method of the present invention, with such step occurring after the prior art processing of FIG. 1.

[0025]FIG. 11 is a view of the FIG. 10 substrate at a processing step subsequent to that of FIG. 10.

[0026]FIG. 12 is a view of the FIG. 10 substrate at a processing step subsequent to that of FIG. 11.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0027] This disclosure of the invention is submitted in furtherance of the constitutional purposes of the U.S. Patent Laws “to promote the progress of science and useful arts” (Article 1, Section 8).

[0028] The present invention encompasses methods for forming planar surfaces over materials having high aspect gaps (such as the material 22 of FIG. 1). As will become more clear from the discussion below, methods of the present invention become increasingly advantageous over prior art methods as aspect ratios of the gaps increase. Accordingly, while methods of the present invention can have applicability and advantages over the prior art for materials having gaps with aspect ratios of less than or equal to three, and can even have advantages for gaps with aspect ratios of less than or equal to one, the invention becomes particularly advantageous when aspect ratios are greater than or equal to five.

[0029] A first embodiment method of the present invention is described with reference to FIGS. 5-8. In referring to FIGS. 5-8, similar numbering to that utilized above in describing the prior art methods of FIGS. 1-4 will be used, with the suffix “a” included to differentiate the structures of FIGS. 5-8 from those of FIGS. 1-4.

[0030] Referring to FIG. 5, a fragment 10 a is illustrated at a processing step subsequent to that of fragment 10 in FIG. 1. Fragment 10 a comprises a substrate 12 a having an upper surface 15 a. Spaced conductive lines 14 a, 16 a, 18 a and 20 a are formed over surface 15 a, and an insulative material 22 a is deposited over and between conductive lines 14 a, 16 a, 18 a and 20 a. Insulative material 22 a can comprise, for example, doped or undoped silicon dioxide formed by CVD from TEOS.

[0031] Conductive lines 14 a, 16 a, 18 a and 20 a form an uneven surface topology over upper surface 15 a. Specifically, lines 14 a, 16 a, 18 a and 20 a correspond to outwardly projecting features, with valleys 24 a corresponding to spaces between the conductive lines. Material 22 a is formed over the uneven surface topology and comprises outwardly extending projections 26 a over the outwardly projecting features of lines 14 a, 16 a, 18 a and 20 a. Material 22 a dips within valleys 24 a to form gaps 28 a over the valleys. Material 22 a has been etched to reduce a height of material 22 a from an initial height 60 (corresponding to a height of material 22 in FIG. 1) to a new height 62. A dashed line 64 in FIG. 5 is provided to show an outline corresponding to the original periphery of material 22 a before the etching.

[0032] In accordance with the present invention, the etching of material 22 a utilizes a high density plasma and an etching gas comprising at least one compound that includes both a halogen and carbon. For purposes of the present invention, a high density plasma is a plasma comprising at least about 1×10⁹ charges/cm³. Such high density plasma can be formed utilizing a so-called high density plasma reactor, which is a reactor that enables separate provision and control of a source power (for generating a plasma) and a bias power (for determining the velocity by which charged particles from the plasma impact a substrate within the reactor). An exemplary high density plasma reactor is an IPS etcher marketed by Applied Materials. Exemplary conditions for utilizing an Applied Materials IPS etcher in a method of the present invention are as follows. A source power is provided to be from about 800 watts to about 1,500 watts, with about 1,000 watts being preferred. A bias power is provided to be from about 500 watts to about 1,600 watts, with about 800 watts being preferred. A pressure within the reactor is provided to be from about 5 mTorr to about 100 mTorr, with about 20 mTorr being preferred. A roof temperature within the reactor is provided to be from about 100° C. to about 250° C., with about 140° C. being preferred. A ring temperature within the reactor is provided to be from about 150° C. to about 350° C., with about 200° C. being preferred. The etching gas comprises C₂F₆ provided at a flow of from about 20 standard cubic centimeters per minute (sccm) to about 100 sccm, with a flow of from about 20 sccm to about 60 sccm being preferred. In particular embodiments of the invention, the etching gas can consist essentially of C₂F₆.

[0033] As the exemplary conditions provided above indicate, the halogen of the etching gas can be fluorine. In general, suitable etching gas compounds can be selected from the group consisting of fluorocarbons and hydrofluorocarbons. In addition to compounds comprising halogen and carbon, the etching gas can include other compounds for controlling particular process parameters. Such other compounds can comprise hydrocarbons, rare gases (such as, for example, helium, neon and argon), nitrogen-containing gases and/or oxygen-containing gases.

[0034] Referring still to FIG. 5, the utilization of a high density plasma in combination with the etching gas comprising both halogen and carbon causes material to be removed from the outer horizontal surfaces 27 a of material 22 a faster than it is removed from within gaps 28 a. Specifically, a polymer 66 is deposited within gaps 28 a and along sidewall peripheries 29 a of the gaps to protect the material 22 a within the gaps from being etched. In the shown embodiment, polymer 66 is deposited in “bread-loaf” structures 68 at upper sidewall peripheral edges of the gaps. Bread-loaf structures 68 which are adjacent to one another can grow into each other to form a cap over gap 28 a which fully protects the portions of material 22 a within the gaps from being etched. Alternatively, adjacent bread-loaf structures 68 may grow to constrict an upper opening of gaps 28 a without fully closing such upper opening. In either event, bread-loaf structures 68 slow a rate of etching within gaps 28 a relative to a rate occurring at outermost horizontal surfaces 27 a. Bread-loaf structures 68 preferably substantially occlude the upper opening of gaps 28 a to substantially prevent removal of material 22 from bottoms 23 a of gaps 28 a during the etching of material 22 from outermost surfaces 27 a.

[0035] It is noted that material 22 a comprises corners 70 at locations where outermost surfaces 27 a join sidewall surfaces 29 a, with such corners being approximately right angles. The etching process of the present invention protects sidewalls 29 a during etching of upper surfaces 27 a and accordingly substantially maintains the right-angle shape of corners 70. The method therefore advantageously substantially avoids faceting of corners 70. Such faceting is undesired in that it can adversely expose the conductive materials of one or more of lines 14 a, 16 a, 18 a or 20 a to the etching conditions.

[0036] The difference in rate of removal of material 22 a from outermost surfaces 27 a relative to the rate of removal from sidewall surfaces 29 a can be controlled by several operational parameters, including, for example, a ratio of bias power to source power within the etcher. Such difference in removal rates can also be controlled by adjusting the amount and type of gases provided within the etcher. For instance, addition of one or both of a nitrogen-containing gas and an oxygen-containing gas can affect a rate of polymer formation, and accordingly affect the difference in rate of removal of material from surface 27 a relative to sidewall surfaces 29 a. Exemplary nitrogen-containing gases are N₂, NO_(x), and NH₃. Exemplary oxygen-containing gases are O₂, O₃ and CO₂.

[0037]FIG. 6 shows fragment 10 a after further etching of material 22 a with the above-described high density plasma and etching gas. As shown, upper elevational level 62 of material 22 a is decreased significantly relative to the initial elevational level 60 of the material. During such etching, the width of gaps 28 a remains substantially unchanged, as does an elevational level of the gap bottoms 23 a.

[0038] Referring to FIG. 7, fragment 10 a is illustrated after material 22 a has been further etched until the upper elevational level 62 of the material is about level with the upper surfaces of conductive lines 14 a, 16 a, 18 a and 20 a. A second material 80 is then formed over conductive lines 14 a, 16 a, 18 a and 20 a, as well as over conductive material 22 a. Material 80 can comprise an insulative material, and can, for example, be silicon dioxide deposited from TEOS. Material 80 has small gaps 82 over the remaining gaps 28 a, with gaps 82 being substantially more shallow than were gaps 28 a in the initially deposited insulative material 22 a (see, for example, FIG. 5). Gaps 82 have bottom peripheries 83 above an elevational level of the uppermost surfaces of conductive lines 14 a, 16 a, 18 a and 20 a.

[0039] In the shown embodiment, polymeric material 66 is left within gaps 28 a during formation of material 80. It is to be understood, however, that the invention encompasses other embodiments (not shown) wherein polymeric material 66 is removed (or partially removed) from within gaps 28 a prior to formation of material 80. Methods for removing material 66 will vary depending on the nature of the polymeric material. In embodiments in which material 66 comprises an organic material, and in which material 22 a is an inorganic oxide, polymeric material 66 can be removed by, for example, ashing.

[0040] Referring to FIG. 8, material 80 is planarized. An exemplary method for planarizing material 80 is chemical-mechanical polishing. After planarization of material 80, conductive lines 14 a, 16 a, 18 a and 20 a are entirely surrounded by insulative material (in embodiments in which materials 22 a and 80 are both insulative materials) and fragment 10 a has an outermost planar surface which can be utilized as a base for formation of additional circuitry (not shown).

[0041] Although the embodiment of FIGS. 5-8 illustrates a material 80 having relatively shallow gaps 83 which can be removed by planarization to form the planar surface of FIG. 8, in other embodiments (not shown) gaps 83 can have a relatively high aspect ratio and be difficult to simply remove by chemical-mechanical planarization. In such other embodiments, the high density plasma etching described with reference to FIG. 5 can be repeated to etch material 80. In such other embodiments, another insulative material can be provided over material 80, and said other insulative material ultimately planarized by chemical-mechanical polishing, or other mechanical processes, or can be subjected to further high density plasma etching of the type described with reference to FIG. 5.

[0042] The embodiment described with reference to FIGS. 5-8 forms a polymer which bread-loafs at an upper portion of gaps 28 a (FIG. 5). Another embodiment of the invention is described with reference to FIG. 9, with the suffix “b” utilized to distinguish the materials of FIG. 9 from those of FIGS. 5-8.

[0043]FIG. 9 illustrates a fragment 10 b at a processing step similar to that described above with reference to FIG. 5. Fragment 10 b differs from the fragment 10 a of FIG. 5 in that the polymer 66 b is formed substantially conformally within gaps 28 b, rather than bread-loafing at an outermost opening of gaps 28 b. Polymer 66 b protects sidewalls 29 b in a manner similar to that by which polymer 66 protected sidewalls 29 a of FIG. 5. Accordingly, fragment 10 b of FIG. 9 can be processed identically to the processing described above with reference to FIG. 5 to ultimately form a structure similar to that shown in FIG. 8. It is noted that although polymer 66 b covers an entirety of sidewalls 29 b in the exemplary shown embodiment, the invention encompasses other embodiments wherein polymer 66 b only covers a bottom portion of sidewalls 29 b.

[0044] Whether it is the embodiment of FIG. 9 that is followed, or that of FIG. 5, or some merger of the two embodiments, can be determined by the parameters chosen for the high density plasma etching described with reference to FIG. 5. Specifically, variation of the etching gases and/or the ratio of bias power to source power can affect whether the etching proceeds more like that described with reference to FIG. 5, or instead like that described with reference to FIG. 9.

[0045] FIGS. 10-12 illustrate yet another embodiment etching method of the present invention. In referring to FIGS. 10-12, similar numbering to that utilized above in describing FIG. 5 will be used, with the suffix “c” utilized to identify structures associated with FIGS. 10-12.

[0046]FIG. 10 shows a fragment 10 c comprising a substrate 12 c having conductive lines 14 c, 16 c, 18 c and 20 c formed thereover. An insulative material 22 c is formed over and between conductive lines 14 c, 16 c, 18 c and 20 c. Material 22 c comprises outer projections 26 c having horizontally extending surfaces 27 c, and gaps 28 c between outwardly projecting portions 26 c. In contrast to the embodiment of FIG. 5, the embodiment of FIG. 10 is not shown at a stage wherein etching of material 22 a has occurred. Rather, a protective material 100 is shown formed over material 22 c and within gaps 28 c. In the shown embodiment, material 100 is provided to a depth which does not entirely fill gaps 28 c. It is to be understood, however, that the invention encompasses other embodiments (not shown) wherein material 100 does fully fill gaps 28 c.

[0047] In an exemplary aspect of the invention, material 22 c is an insulative material utilized as an electrical insulator between conductive lines 14 c, 16 c, 18 c and 20 c. In such aspects of the invention, material 100 can also comprise an insulative material. Material 100 can comprise, for example, polymeric materials formed by deposition from one or more of hydrocarbon precursors, fluorocarbon precursors, and hydrofluorocarbon precursors. Alternatively, material 100 can comprise photoresist. In yet other alternative embodiments, material 100 can comprise silicon dioxide formed by Flow-Fill™ processes. Flowfill™ technology has been developed by Trikon Technology of Bristol, U.K.

[0048] Referring to FIG. 11, material 100 is removed from over surfaces 27 c. Such can be accomplished by, for example, chemical-mechanical polishing. After removal from over surfaces 27 c, some material 100 remains within gaps 28 c to protect sidewall surfaces 29 c from a subsequent etch.

[0049] Referring to FIG. 12, material 22 c is etched utilizing, for example, the high density plasma etch described above with reference to FIG. 5. Such removes material 22 c from an initial elevational level 60 c and can form polymers 66 c within gaps 28 c. Protective material 100 provides additional protection for sidewalls 29 c during the etching process beyond that which is provided merely by the bread-loafed polymer 66 c. It is noted that material 100 can comprise a composition which is etched by the high-density etching process so that material 100 is removed during removal of material 22 c. If material 100 is not removed during removal of material 22 c, projections of material 100 will ultimately result in the locations of gaps 28 c as material 22 c is removed from adjacent the material 100. Such projections can be later removed by polishing processes, such as, for example, chemical-mechanical polishing.

[0050] Fragment 10 c can be processed according to methodologies similar to those described above with reference to FIGS. 5-8 to form a structure similar to that of FIG. 8.

[0051] Although the invention is described above with reference to methods of forming an insulative material over and between conductive lines, it is to be understood that the invention has general application to methods of material etching, and can be utilized for etching conductive materials. For instance, if conductive materials are formed having high aspect ratio gaps extending therein, methods of the present invention can be utilized to protect sidewalls of the gaps while the conductive material is etched. Such protection can substantially prevent the gaps from being extended during etching of the conductive material.

[0052] In compliance with the statute, the invention has been described in language more or less specific as to structural and methodical features. It is to be understood, however, that the invention is not limited to the specific features shown and described, since the means herein disclosed comprise preferred forms of putting the invention into effect. The invention is, therefore, claimed in any of its forms or modifications within the proper scope of the appended claims appropriately interpreted in accordance with the doctrine of equivalents. 

1. A semiconductor processing method of forming a material over an uneven surface topology, comprising: providing a substrate having the uneven surface topology, the uneven surface topology comprising a valley between a pair of outwardly projecting features; forming a layer of material over the uneven surface topology, the layer comprising outwardly projecting portions over the outwardly projecting features of the surface topology and having a gap over the valley, the gap having a lowestmost portion; and etching the layer, the etching forming protective material within the gap while removing an outermost surface of the layer, the etching substantially not removing material of the layer from the lowestmost portion of the gap.
 2. The method of claim 1 wherein the material of the layer is an electrically insulative material.
 3. The method of claim 1 wherein the etching comprises high density plasma etching.
 4. The method of claim 1 wherein the material of the layer comprises silicon dioxide and is formed by chemical vapor deposition from TEOS.
 5. The method of claim 1 wherein the etching gas comprises at least one compound that includes both a halogen and carbon.
 6. The method of claim 1 wherein the etching occurs in a high density plasma reactor utilizing an etching gas, a source power of from about 800 watts to about 1500 watts, a bias power of from about 500 watts to about 1600 watts, a pressure of from about 5 mTorr to about 100 mTorr, a roof temperature of from about 100° C. to about 250° C. and a ring temperature of from about 150° C. to about 350° C.
 7. The method of claim 6 wherein the etching gas comprises a gas selected from the group consisting of fluorocarbons, hydrofluorocarbons, and mixtures thereof.
 8. The method of claim 6 wherein the etching gas consists essentially of one or both of fluorocarbon compounds and hydrofluorocarbon compounds.
 9. The method of claim 6 wherein the plasma is a high density plasma comprising at least about 1×10⁹ charges/cm³.
 10. A semiconductor processing method of forming a material over metal-comprising lines, comprising: providing a first insulative material substrate; forming a pair of spaced metal-comprising lines over the substrate; the spaced metal-comprising lines defining an uneven surface topology which comprises the lines and a valley between the lines; forming a layer of second insulative material over the uneven surface topology, the layer comprising outwardly projecting portions over the lines and having a gap over the valley; and subjecting the layer of second insulative material to an etch which forms a protective material at the bottom of the gap; the protective material substantially preventing the second insulative material from being etched from a bottom of the gap.
 11. The method of claim 10 wherein the metal-comprising lines consist essentially of materials selected from the group consisting of one or more of aluminum, copper, copper alloys and aluminum alloys.
 12. The method of claim 10 wherein the first and second insulative materials comprise a common composition, said common composition being either doped silicon dioxide or undoped silicon dioxide.
 13. The method of claim 10 wherein the etching comprises high density plasma etching utilizing an etching gas that includes at least one compound comprising both a halogen and carbon.
 14. The method of claim 13 wherein the etching occurs in a high density plasma reactor utilizing a source power of from about 800 watts to about 1500 watts, a bias power of from about 500 watts to about 1600 watts, a pressure of from about 5 mTorr to about 100 mtorr, a roof temperature of from about 100° C. to about 250° C. and a ring temperature of from about 150° C. to about 350° C.
 15. The method of claim 10 wherein the high density plasma comprises at least about 1×10⁹ charges/cm³.
 16. The method of claim 10 wherein the gap has an aspect ratio of at least
 1. 17. The method of claim 10 wherein the gap has an aspect ratio of at least
 3. 18. The method of claim 10 wherein the gap has an aspect ratio of at least
 5. 19. A semiconductor processing method of forming and etching a material, comprising: providing a substrate having spaced projections extending thereover; forming a first layer of a first insulative material over the projections, the first layer of first insulative material comprising outwardly extending portions over the projections of the substrate and having a gap over the space between the projections; depositing a first protective material within the gap to at least partially fill the gap; and after the depositing subjecting the first layer to a first plasma etch utilizing an etching gas, the first plasma etch forming a second protective material within the gap while removing an outermost surface of the first layer of first insulative material, the first and second protective materials preventing first insulative material of the first layer from being removed from a bottom of the gap.
 20. The method of claim 19 wherein the first insulative material comprises either doped or undoped silicon dioxide and is formed by chemical vapor deposition from TEOS.
 21. The method of claim 19 wherein the first plasma etch occurs in a high density plasma reactor utilizing a source power of from about 800 watts to about 1500 watts, a bias power of from about 500 watts to about 1600 watts, a pressure of from about 5 mTorr to about 100 mTorr, a roof temperature of from about 100° C. to about 250° C., a ring temperature of from about 150° C. to about 350° C., and an etching gas comprising at least one of a fluorocarbon or a hydrofluorocarbon.
 22. The method of claim 19 wherein the depositing the protective material comprises chemical vapor deposition utilizing a hydrocarbon precursor material.
 23. The method of claim 19 further comprising: after subjecting the first insulative material to the plasma etch, providing a second layer of a second insulative material over the first insulative material; and subjecting the second layer to a second plasma etch.
 24. The method of claim 23 wherein the first and second insulative materials comprise a common insulative material, and wherein the first and second plasma etches utilize common etching conditions.
 25. A semiconductor processing method of forming an insulative material over and between conductive lines, comprising: providing a substrate having a pair of spaced conductive lines formed thereover; forming a first layer of insulative material over the substrate and the spaced conductive lines, the first layer comprising outwardly projecting portions over the lines and having a gap over the space between the lines; subjecting the first layer to a first high density plasma etch to remove at least some of the material of the first layer from over the conductive lines; the first plasma etch utilizing an etching gas that comprises at least one compound that includes both a halogen and carbon and substantially not etching the insulative material of the first layer from the bottom of the gap; and providing a second layer of insulative material over the etched first layer.
 26. The method of claim 25 wherein the first plasma etch occludes the gap with a protective material.
 27. The method of claim 25 further comprising, before subjecting the first layer to the plasma etch, depositing a protective material within the gap to at least partially fill the cap.
 28. The method of claim 27 wherein the depositing the protective material comprises chemical vapor deposition utilizing a hydrocarbon precursor material.
 29. The method of claim 25 further comprising subjecting the second layer to a second high density plasma etch.
 30. The method of claim 29 wherein the first and second layers comprise the same material, and wherein the first and second plasma etches utilize the same etching conditions.
 31. The method of claim 25 wherein the material of the first layer comprises silicon dioxide and is formed by chemical vapor deposition from TEOS.
 32. The method of claim 25 wherein the first plasma etch occurs in a high density plasma reactor utilizing a source power of from about 800 watts to about 1500 watts, a bias power of from about 500 watts to about 1600 watts, a pressure of from about 5 mTorr to about 100 mTorr, a roof temperature of from about 100° C. to about 250° C. and a ring temperature of from about 150° C. to about 350° C.
 33. The method of claim 32 wherein the etching gas comprises a gas selected from the group consisting of fluorocarbons, hydrofluorocarbons, and mixtures thereof. 